PEEK5600G particles Relying on the previous ten years of experience in the PEEK industry, the company has officially entered the polymerization production of PEEK resin, which can provide stronger raw material guarantees for PEEK parts and profiles and create advantageous conditions. At the same time, through the research and development and production of profiles and parts, it will also promote the research and development and production of raw material resin polymerization. The company has a full industrial chain enterprise with the ability to polymerize PEEK resin raw materials, modified granulation, continuous extrusion of plate and rod profiles, and research and development and production of finished parts. The cost and technical advantages are very outstanding! As an advanced engineering plastic, PEEK...
Relying on the previous ten years of experience in the PEEK industry, the company has officially entered the polymerization production of PEEK resin, which can provide stronger raw material guarantees for PEEK parts and profiles and create advantageous conditions. At the same time, through the research and development and production of profiles and parts, it will also promote the research and development and production of raw material resin polymerization. The company has a full industrial chain enterprise with the ability to polymerize PEEK resin raw materials, modified granulation, continuous extrusion of plate and rod profiles, and research and development and production of finished parts. The cost and technical advantages are very outstanding! As an advanced engineering plastic, PEEK has good machinability, flame retardancy, non-toxicity, wear resistance, corrosion resistance and other characteristics. It plays an important role in weight reduction, effectively extending the service life of components, and optimizing component utilization, and the promotion of downstream applications is accelerated.
PEEK Mechanical Properties
Mechanical properties
project
Test standard or instrumen
unit
PEEK5600G
PEEK5600GF30
PEEK5600CF30
PEEK5600LF30
Tensile strength (23℃)
ISO527
MPa
90
155
210
134
Bending strength (23℃)
ISO 178
MPa
150
212
298
186
Compression strength (23℃)
ISO 604
MPa
118
215
240
150
Lzod impact strength (unnotched)
ISO 180/IU
kJ/m 2
No breakage
51
40
32
PEEK Thermal Properties
Thermal performance
project
Test standard or instrumen
unit
PEEK5600G
PEEK5600GF30
PEEK5600CF30
PEEK5600LF30
Melting point
ISO 11357
℃
343
343
343
343
Heat Deflection Temperature
ISO 75-f
℃
163
315
315
293
Continuous use temperature
UL 74685
℃
260
260
260
260
Coefficient of thermal expansion
ASTM D696
10 -5℃
4.7
2.2
1.5
2.2
Flammability level
UL 94
V-0@mm
1.5
1.5
1.5
0.75
PEEK Electrical Properties
Electrical performance
project
Test standard or instrumen
unit
PEEK5600G
PEEK5600GF30
PEEK5600CF30
PEEK5600LF30
Dielectric strength
IEC 60243-1
kV/mm
18
19
Dielectric constant
IEC60250
—
3.2
3.3
Surface resistivity
IEC 90093
Oh
1015
1015
105
106
PEEK Other Properties
Other features
project
Test standards or instruments
unit
PEEK5600G
PEEK5600GF30
PEEK5600CF30
PEEK5600LF30
density
ISO 1183
g/cm3
1.3±0.02
1.5±0.02
1.4±0.02
1.43±0.02
Rockwell hardness
ISO 2039
HRR
118
119
121
108
Friction coefficient
ASTM D3702
－
0.30-0.38
0.38-0.46
0.28
0.18
Water absorption rate(25℃.24Hrs)
ISO 62
%
0.15
0.11
0.06
0.06
Molding shrinkage (25-24℃)
3mm thickness, flow direction at 170℃
%
1.2
0.4
0.1
0.3
Perpendicular to the flow direction (larger after saturated crystallization)
%
1.5
0.8
0.5
0.5
The performance indicators of this material are injection molding indicators. If necessary, please call our technical department for more detailed technical indicators!